Heat Shrink Tubing without Glue diameter 6,4mm 2:1 White

Polyolefin Sheath 2:1 shrink flexible, with high ratio of narrowing suited to various applications given its particular adaptability to all forms. Widely used for insulation and identification in electrical wiring, for cable assembly or as simple mechanical protection. It is also suitable for all those applications where a relatively low shrinkage temperature is required.

Features:
- Polyolefin
- Shrinkage factor: 2:1
- Self extinguishing
- Suitable for any use
- Highly flexible
- Tensile strength: = 17 MPa
- Elongation: = 500%
- Secant modulus: 175 MPa
- Specific weight: 1,30g / cm³
- Elongation after Heat Aging: 500%
- Tensile strength after thermal aging (168 hours at 175 ° C): 13 MPa
- Elongation after Heat Shock (4 hours at 250 ° C): No cracking
- Tensile strength after thermal shock (4 hours at 250 ° C): 13 MPa
- Low Temperature Flexibility: It does not break at -55 ° C
- Flammability: Self-extinguishing UL 224
- Dielectric Strength: 24 kV/mm
- Volume Resistivity: >= 10^14 Ohm/cm
- Weathering: Non-corrosive
- Water absorption: 0.15%

Certifications:
- Meets MIL - DTL - 123053/5
- Compliant with: RoHS

Application:
- Operating temperature: from -55°C to + 135°C
- Minimum shrinkage temperature: + 90°C
- Longitudinal variation: 0 ± 10% maximum